| 布氏硬度 HB | 洛氏硬度 | Tidak ada komentar 硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| SDM | HAM | SDM | HAM | ||||
| 86.6 | 70.0 | tahun 1037 | 78.5 | 55.0 | 599 | ||
| 86.3 | 69.5 | tahun 1017 | 78.2 | 54.5 | 589 | ||
| 86.1 | 69.0 | 997 | 77.9 | 54.0 | 579 | ||
| 85.8 | 68.5 | 978 | 77.7 | 53.5 | 570 | ||
| 85.5 | 68.0 | 959 | 77.4 | 53.0 | 561 | ||
| 85.2 | 67.5 | 941 | 77.1 | 52.5 | 551 | ||
| 85.0 | 67.0 | 923 | 76.9 | 52.0 | 543 | ||
| 84.7 | 66.5 | tahun 906 | 76.6 | 51.5 | 534 | ||
| 84.4 | 66.0 | 889 | 501 | 76.3 | 51.0 | 525 | |
| 84.1 | 65.5 | 872 | 494 | 76.1 | 50.5 | 517 | |
| 83.9 | 65.0 | 856 | 488 | 75.8 | 50.0 | 509 | |
| 83.6 | 64.5 | 840 | 481 | 75.5 | 49.5 | 501 | |
| 83.3 | 64.0 | 825 | 474 | 75.3 | 49.0 | 493 | |
| 83.1 | 63.5 | 810 | 468 | 75.0 | 48.5 | 485 | |
| 82.8 | 63.0 | 795 | 461 | 74.7 | 48.0 | 478 | |
| 82.5 | 62.5 | 780 | 455 | 74.5 | 47.5 | 470 | |
| 82.2 | 62.0 | 766 | 449 | 74.2 | 47.0 | 463 | |
| 82.0 | 61.5 | 752 | 442 | 73.9 | 46.5 | 456 | |
| 81.7 | 61.0 | 739 | 436 | 73.7 | 46.0 | 449 | |
| 81.4 | 60.5 | 726 | 430 | 73.4 | 45.5 | 443 | |
| 81.2 | 60.0 | 713 | 424 | 73.2 | 45.0 | 436 | |
| 80.9 | 59.5 | 700 | 418 | 72.9 | 44.5 | 429 | |
| 80.6 | 59.0 | 688 | 413 | 72.6 | 44.0 | 423 | |
| 80.3 | 58.5 | 676 | 407 | 72.4 | 43.5 | 417 | |
| 80.1 | 58.0 | 664 | 401 | 72.1 | 43.0 | 411 | |
| 79.8 | 57.5 | 653 | 396 | 71.8 | 42.5 | 405 | |
| 79.5 | 57.0 | 642 | 391 | 71.6 | 42.0 | 399 | |
| 79.3 | 56.5 | 631 | 385 | 71.3 | 41.5 | 393 | |
| 79.0 | 56.0 | 620 | 380 | 71.1 | 41.0 | 388 | |
| 78.7 | 55.5 | 609 | 375 | 70.8 | 40.5 | 382 | |
Tabel konversi nilai kekerasan bahan logam besi
| 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | 布氏硬度 HB | 洛氏硬度 | 维氏硬度 HV | ||
| SDM | HAM | SDM | HAM | ||||
| 370 | 70.5 | 40.0 | 377 | 269 | 28.0 | 274 | |
| 365 | 70.3 | 39.5 | 372 | 266 | 27.5 | 271 | |
| 360 | 70.0 | 39.0 | 367 | 263 | 27.0 | 268 | |
| 355 | 38.5 | 362 | 260 | 26.5 | 264 | ||
| 350 | 38.0 | 351 | 257 | 26.0 | 261 | ||
| 345 | 37.5 | 352 | 254 | 25.5 | 258 | ||
| 341 | 37.0 | 347 | 251 | 25.0 | 255 | ||
| 336 | 36.5 | 342 | 248 | 24.5 | 252 | ||
| 332 | 36.0 | 338 | 245 | 24.0 | 249 | ||
| 327 | 35.5 | 333 | 242 | 23.5 | 246 | ||
| 323 | 35.0 | 329 | 240 | 23.0 | 243 | ||
| 318 | 34.5 | 324 | 237 | 22.5 | 240 | ||
| 314 | 34.0 | 320 | 234 | 22.0 | 237 | ||
| 310 | 33.5 | 316 | 232 | 21.5 | 234 | ||
| 306 | 33.0 | 312 | 229 | 21.0 | 231 | ||
| 302 | 32.5 | 308 | 227 | 20.5 | 229 | ||
| 298 | 32.0 | 304 | 225 | 20.0 | 226 | ||
| 294 | 31.5 | 300 | 222 | 19.5 | 223 | ||
| 291 | 31.0 | 296 | 220 | 19.0 | 221 | ||
| 287 | 30.5 | 292 | 218 | 18.5 | 218 | ||
| 283 | 30.0 | 289 | 216 | 18.0 | 216 | ||
| 280 | 29.5 | 285 | 214 | 17.5 | 214 | ||
| 276 | 29.0 | 281 | 211 | 17.0 | 211 | ||
| 273 | 28.5 | 278 | |||||
Catatan:
1. Kekerasan Brinell: Terutama digunakan untuk mengukur kekerasan coran, tempaan, komponen logam non-ferrous, billet canai panas, dan komponen anil. Rentang pengukurannya adalah ≥HB450.
2. Kekerasan Rockwell: HRA terutama digunakan untuk spesimen dengan kekerasan tinggi guna mengukur kekerasan permukaan material dan permukaan dengan kekerasan lebih tinggi dari HRC67, seperti karbida semen, baja nitridasi, dll. Rentang pengukurannya adalah HRA>70. HRC terutama digunakan untuk mengukur kekerasan komponen baja (seperti baja karbon, baja perkakas, baja paduan, dll.) setelah pendinginan atau tempering. Rentang pengukurannya adalah HRC20~67.
3. Kekerasan Vickers: digunakan untuk mengukur kekerasan bagian tipis dan bagian pelat baja, dan juga dapat digunakan untuk mengukur kekerasan bagian yang permukaannya dikeraskan seperti karburisasi, sianidasi, dan nitridasi.
Waktu posting: 07-Apr-2024